Synthesis, Structural and Morphological Studies of CdS Nanopowder

Santhosh Kumar N, Govinda D and Thirumala Rao G


Hexagonal wurtzite structured CdS nanopowder was synthesized by using chemical precipitation method. Various spectroscopic technics were used for the characterization of the prepared sample. X-ray diffraction pattern shows the high intense crystalline peaks and the average crystallite size is found to be 19 nm. SEM micrographs reveal the non-uniformly distributed spherical shaped structures. EDS analysis confirms the stoichiometric composition and presence of target elements. FT-IR spectrum exhibited a metal sulfide band at 615 cm–1 and other functional groups.


Avertissement: testCe résumé a été traduit à l'aide d'outils d'intelligence artificielle et n'a pas encore été examiné ni vérifié

Indexé dans

  • CASS
  • Google Scholar
  • Ouvrir la porte J
  • Infrastructure nationale du savoir de Chine (CNKI)
  • CiterFactor
  • Cosmos SI
  • Bibliothèque de revues électroniques
  • Répertoire d’indexation des revues de recherche (DRJI)
  • Laboratoires secrets des moteurs de recherche
  • ICMJE

Voir plus

Flyer