Fatigue Corrosion of 316lss Different Chromium Content

D. Bubesh Kumar, K. G. Muthurajan


Fatigue corrosion of 316LSS having different chromium content, the fatigue corrosion was carried out in different chromium content 10% to 16% 316L stainless steel. The test was carried out in surface impact fatigue corrosion machine. The pitting life was calculated, it gives the fatigue corrosion resistance of 316LSS and S-N curve was plotted.